Method and apparatus for manufacturing flexible light emitting device

ABSTRACT

According to a flexible light-emitting device production method of the present disclosure, after an intermediate region ( 30   i ) and a flexible substrate region ( 30   d ) of a plastic film ( 30 ) of a multilayer stack ( 100 ) are divided, the interface between the flexible substrate region ( 30   d ) and a glass base ( 10 ) is irradiated with lift-off light. The multilayer stack ( 100 ) is separated into the first portion ( 110 ) and the second portion ( 120 ) while the multilayer stack ( 100 ) is kept in contact with the stage ( 210 ). The first portion ( 110 ) includes a plurality of light-emitting devices ( 1000 ) which are in contact with the stage ( 210 ). The light-emitting devices ( 1000 ) include a plurality of functional layer regions ( 20 ) and the flexible substrate region ( 30   d ). The second portion ( 120 ) includes the glass base ( 10 ) and the intermediate region ( 30   i ). The step of irradiating with the lift-off light includes forming the lift-off light from a plurality of arranged light sources and temporally and spatially modulating a power of the plurality of lift-off light sources according to a shape of the flexible substrate region of the synthetic resin film such that the irradiation intensity of the lift-off light for at least part of the interface between the intermediate region ( 30   i ) and the glass base ( 10 ) is lower than the irradiation intensity of the lift-off light for the interface between the flexible substrate region ( 30   d ) and the glass base ( 10 ).

TECHNICAL FIELD

The present disclosure relates to a method and apparatus for producing aflexible light-emitting device.

BACKGROUND ART

A typical example of the flexible display includes a film which is madeof a synthetic resin such as polyimide (hereinafter, referred to as“plastic film”), and elements supported by the plastic film, such asTFTs (Thin Film Transistors) and OLEDs (Organic Light Emitting Diodes).The plastic film functions as a flexible substrate. The flexible displayis encapsulated with a gas barrier film (encapsulation film) because anorganic semiconductor layer which is a constituent of the OLED is likelyto deteriorate due to water vapor.

Production of the above-described flexible display is carried out usinga glass base on which a plastic film is formed over the upper surface.The glass base functions as a support (carrier) for keeping the shape ofthe plastic film flat during the production process. TFT devices,light-emitting devices such as OLEDs, a gas barrier film, and the otherconstituents are formed on the plastic film, whereby the structure of aflexible display is realized while it is supported by the glass base.Thereafter, the flexible display is delaminated from the glass base andgains flexibility. The entirety of a portion in which TFT devices andlight-emitting devices such as OLEDs are arrayed can be referred to as“functional layer region”.

According to the prior art, a sheet-like structure including a pluralityof flexible display is delaminated from a glass base, and thereafter,optical parts and other constituents are mounted to this sheet-likestructure. Thereafter, the sheet-like structure is divided into aplurality of flexible devices. This dividing is realized by, forexample, laser beam irradiation.

Patent Document No. 1 discloses the method of irradiating the interfacebetween each flexible display and the glass base with laser light inorder to delaminate each flexible display from the glass base(supporting substrate). According to the method disclosed in PatentDocument No. 1, after irradiation with the lift-off light, respectiveflexible displays are divided from one another, and each of the flexibledisplays is delaminated from the glass base.

CITATION LIST Patent Literature

Patent Document No. 1: Japanese Laid-Open Patent Publication No.2014-48619

SUMMARY OF INVENTION Technical Problem

According to the conventional production method, the dividing by meansof laser beam irradiation is carried out after expensive parts, forexample, encapsulation film, polarizer, and/or heat radiation sheet, aremounted to a sheet-like structure including a plurality of flexibledisplays. Therefore, unnecessary portions divided by laser beamirradiation, i.e., portions which are not to be constituents of a finaldisplay, are quite useless. Also, there is a problem that, after beingdelaminated from the glass base, it is difficult to handle a pluralityof flexible displays which have no rigidity.

Such a problem is not limited to flexible displays which include OLEDsas light-emitting devices but can arise in producing a flexiblelight-emitting device which includes a micro LED (μLED) formed as alight-emitting device using inorganic semiconductor materials.

The present disclosure provides a method and apparatus for producing aflexible light-emitting device which are capable of solving theabove-described problems.

Solution to Problem

The flexible light-emitting device production method of the presentdisclosure includes, in an exemplary embodiment: comprises, providing amultilayer stack which has a first surface and a second surface, themultilayer stack including a glass base which defines the first surface,a functional layer region including a TFT layer and a light-emittingdevice layer, a synthetic resin film provided between the glass base andthe functional layer region and bound to the glass base, the syntheticresin film including a flexible substrate region supporting thefunctional layer region and an intermediate region surrounding theflexible substrate region, and a protection sheet which covers thefunctional layer region and which defines the second surface, dividingthe intermediate region and the flexible substrate region of thesynthetic resin film from each other, irradiating an interface betweenthe synthetic resin film and the glass base with lift-off light, andseparating the multilayer stack into a first portion and a secondportion by increasing a distance from a stage to the glass base whilethe second surface of the multilayer stack is kept in contact with thestage. The first portion of the multilayer stack includes alight-emitting device which is in contact with the stage, thelight-emitting device including the functional layer region and theflexible substrate region of the synthetic resin film. The secondportion of the multilayer stack includes the glass base and theintermediate region of the synthetic resin film. The method furthercomprises irradiating the interface between the synthetic resin film andthe glass base with the lift-off light includes forming the lift-offlight from a plurality of arranged light sources and temporally andspatially modulating a power of the plurality of light sources accordingto a shape of the flexible substrate region of the synthetic resin filmsuch that an irradiation intensity of the lift-off light for at leastpart of an interface between the intermediate region of the syntheticresin film and the glass base is lower than an irradiation intensity ofthe lift-off light for the interface between the flexible substrateregion of the synthetic resin film and the glass base.

In one embodiment, the lift-off light is incoherent light.

In one embodiment, the light-emitting device layer includes a pluralityof arrayed micro LEDs, and the lift-off light is laser light.

In one embodiment, a shape of the flexible substrate region of thesynthetic resin film has a cutout, a protrusion, and/or a curved contourwhen viewed in a direction perpendicular to the first surface.

In one embodiment, a number of the flexible substrate region of thesynthetic resin film is plural, and a number of the light-emittingdevice included in the first portion of the multilayer stack is plural.

In one embodiment, the plurality of light sources are a plurality oflight emitting diode devices, and irradiating the interface between thesynthetic resin film and the glass base with the lift-off light includesmodulating a driving current flowing through each of the plurality oflight emitting diode devices, thereby temporally and/or spatiallymodulating the irradiation intensity of the lift-off light.

In one embodiment, the plurality of light emitting diode devices arearranged in a single row or a plurality of rows.

In one embodiment, an arrangement pitch of the plurality of lightemitting diode devices is in a range of not less than 3 mm and not morethan 10 mm.

In one embodiment, the lift-off light is a line beam extending in afirst direction which is parallel to a perimeter of the glass base, andirradiating the interface between the synthetic resin film and the glassbase with the lift-off light includes moving an irradiation region onthe interface which is to be irradiated with the lift-off light in asecond direction which is transverse to the first direction.

In one embodiment, the lift-off light is plane-like light extending in afirst direction and a second direction, the first direction beingparallel to a perimeter of the glass base, the second direction beingtransverse to the first direction, and irradiating the interface betweenthe synthetic resin film and the glass base with the lift-off lightincludes moving or not-moving irradiation region on the interface whichis to be irradiated with the lift-off light.

In one embodiment, the at least part of the interface between theintermediate region of the synthetic resin film and the glass baseincludes a plurality of parallel stripe regions extending in the firstdirection, and any of the plurality of parallel stripe regions includesa large-width portion and/or a narrow-width portion.

In one embodiment, the at least part of the interface between theintermediate region of the synthetic resin film and the glass baseincludes a plurality of parallel stripe regions extending in the seconddirection, and any of the plurality of parallel stripe regions includesa large-width portion and/or a narrow-width portion.

In one embodiment, the at least part of the interface between theintermediate region of the synthetic resin film and the glass base has awidth which is not less than 50% of a width of the intermediate region.

In one embodiment, the at least part of the interface between theintermediate region of the synthetic resin film and the glass base has awidth which is not less than 1 mm.

In one embodiment, the difference between an irradiation intensity ofthe lift-off light in the at least part of the interface between theintermediate region of the synthetic resin film and the glass base andan irradiation intensity of the lift-off light for the interface betweenthe flexible substrate region of the synthetic resin film and the glassbase is not less than 50 mJ/cm².

In one embodiment, the method further comprises, after separating themultilayer stack into the first portion and the second portion,performing a process on the light-emitting device which is in contactwith the stage.

The flexible light-emitting device production apparatus of the presentdisclosure includes, in an exemplary embodiment: a stage for supportinga multilayer stack which has a first surface and a second surface, themultilayer stack including a glass base which defines the first surface,a functional layer region including a TFT layer and a light-emittingdevice layer, a synthetic resin film provided between the glass base andthe functional layer region and bound to the glass base, the syntheticresin film including a flexible substrate region supporting thefunctional layer region and an intermediate region surrounding theflexible substrate region, and a protection sheet which covers thefunctional layer region and which defines the second surface, theintermediate region and the flexible substrate region of the syntheticresin film being divided from each other, and a lift-off lightirradiation unit for irradiating with lift-off light an interfacebetween the synthetic resin film and the glass base in the multilayerstack supported by the stage. The lift-off light irradiation unitincludes a plurality of arranged light sources for forming the lift-offlight. The lift-off light irradiation unit temporally and spatiallymodulates a power of the plurality of light sources according to a shapeof the flexible substrate region of the synthetic resin film such thatan irradiation intensity of the lift-off light for at least part of aninterface between the intermediate region of the synthetic resin filmand the glass base is lower than an irradiation intensity of thelift-off light for the interface between the flexible substrate regionof the synthetic resin film and the glass base.

In one embodiment, each of the plurality of arranged light sources is anincoherent light source.

In one embodiment, the light-emitting device layer includes a pluralityof arrayed micro LEDs, and each of the plurality of light sources is asemiconductor laser device.

In one embodiment, the plurality of light sources are a plurality oflight emitting diode devices, and the lift-off light irradiation unitincludes a driving circuit for modulating a driving current flowingthrough each of the plurality of light emitting diode devices, therebytemporally and/or spatially modulating the irradiation intensity of thelift-off light.

In one embodiment, the plurality of light emitting diode devices arearranged in a single row or a plurality of rows.

In one embodiment, an arrangement pitch of the plurality of lightemitting diode devices is in a range of not less than 3 mm and not morethan 10 mm.

In one embodiment, the apparatus further comprises an actuator forincreasing a distance from the stage to the glass base while the stageis kept in contact with the second surface of the multilayer stack,thereby separating the multilayer stack into a first portion and asecond portion. The first portion of the multilayer stack includes alight-emitting device which is in contact with the stage. Thelight-emitting device includes the functional layer region and theflexible substrate region of the synthetic resin film, and the secondportion of the multilayer stack includes the glass base and theintermediate region of the synthetic resin film.

The lift-off light irradiation apparatus for irradiating an interfacebetween a glass base and a synthetic resin film formed on the glass basewith lift-off light of the present disclosure includes, in an exemplaryembodiment: a plurality of light emitting diodes each emittingultra-violet light to form the lift-off light, a driving circuit fordriving each of the plurality of light emitting diodes, and a controllerconfigured to control the driving circuit to modulate temporally andspatially an intensity of the lift-off light.

Advantageous Effects of Invention

According to an embodiment of the present invention, a novel method forproducing a flexible light-emitting device which is capable of solvingthe above-described problems is provided.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A is a plan view showing a configuration example of a multilayerstack used in a flexible light-emitting device production method of thepresent disclosure.

FIG. 1B is a cross-sectional view of the multilayer stack taken alongline B-B of FIG. 1A.

FIG. 1C is a plan view showing a configuration example of a plastic filmin the multilayer stack.

FIG. 1D is a plan view showing another configuration example of aplastic film in the multilayer stack.

FIG. 1E is a cross-sectional view showing another example of themultilayer stack.

FIG. 1F is a cross-sectional view showing still another example of themultilayer stack.

FIG. 2 is a cross-sectional view schematically showing the dividingpositions in the multilayer stack.

FIG. 3A is a diagram schematically showing a state immediately before astage supports a multilayer stack.

FIG. 3B is a diagram schematically showing a state where the stagesupports the multilayer stack.

FIG. 3C is a diagram schematically showing that the interface between aglass base and a plastic film of the multilayer stack with lift-offlight.

FIG. 4 is a perspective view schematically showing irradiation of amultilayer stack with laser light (lift-off light) emitted from a laserlight source of a lift-off light irradiation unit.

FIG. 5 is a block diagram schematically showing the flow of signals,data and instructions in the lift-off light irradiation unit.

FIG. 6 is a perspective view schematically showing a basic configurationof a semiconductor laser device which can be used in a line beam source.

FIG. 7A is a diagram schematically showing a configuration example of aline beam source and an example of the light intensity distribution oflaser light emitted from a semiconductor laser device during scanning.

FIG. 7B is a diagram schematically showing a configuration example of aline beam source and another example of the light intensity distributionof laser light emitted from a semiconductor laser device duringscanning.

FIG. 8 is a perspective view schematically showing another configurationexample of the line beam source.

FIG. 9 is a diagram schematically showing an example of the distributionin the Y-axis direction of the irradiation intensity of the lift-offlight.

FIG. 10 is a diagram schematically showing another example of thedistribution in the Y-axis direction of the irradiation intensity of thelift-off light.

FIG. 11 is a diagram schematically showing still another example of thedistribution in the Y-axis direction of the irradiation intensity of thelift-off light.

FIG. 12 is a diagram schematically showing still another example of thedistribution in the Y-axis direction of the irradiation intensity of thelift-off light.

FIG. 13 is a diagram schematically showing an example of thedistribution in the X-axis direction (scanning direction) of theirradiation intensity of the lift-off light.

FIG. 14 is a diagram schematically showing another example of thedistribution in the X-axis direction of the irradiation intensity of thelift-off light.

FIG. 15A is a diagram schematically showing still another example of thedistribution in the X-axis direction of the irradiation intensity of thelift-off light.

FIG. 15B is a diagram schematically showing still another example of thedistribution in the X-axis direction of the irradiation intensity of thelift-off light.

FIG. 16A is a cross-sectional view schematically showing the multilayerstack before the multilayer stack is separated into the first portionand the second portion after irradiation with lift-off light.

FIG. 16B is a cross-sectional view schematically showing the multilayerstack separated into the first portion and the second portion.

FIG. 17 is a perspective view showing the glass base separated from themultilayer stack by a delaminating apparatus.

FIG. 18 is a perspective view showing removal of the glass base from thestage.

FIG. 19 is a perspective view showing the stage from which the glassbase has been removed.

FIG. 20 is a cross-sectional view showing the stage from which the glassbase has been removed.

FIG. 21 is a cross-sectional view showing flexible light-emittingdevices detached from the stage.

FIG. 22 is a cross-sectional view showing another protection sheet boundto a plurality of Light-emitting devices which are in contact with thestage.

FIG. 23 is a cross-sectional view showing a carrier sheet carrying aplurality of parts which are to be mounted to the plurality ofLight-emitting devices.

FIG. 24A is a cross-sectional view illustrating a step of the flexiblelight-emitting device production method in an embodiment of the presentdisclosure.

FIG. 24B is a cross-sectional view illustrating a step of the flexiblelight-emitting device production method in an embodiment of the presentdisclosure.

FIG. 24C is a cross-sectional view illustrating a step of the flexiblelight-emitting device production method in an embodiment of the presentdisclosure.

FIG. 24D is a cross-sectional view illustrating a step of the flexiblelight-emitting device production method in an embodiment of the presentdisclosure.

FIG. 25 is an equivalent circuit diagram of a single sub-pixel in aflexible light-emitting device.

FIG. 26 is a perspective view of the multilayer stack in the middle ofthe production process.

FIG. 27A is a diagram schematically showing the upper surface of a linebeam source 214 which includes a single column of light emitting diodedevices arrayed in Y-axis direction.

FIG. 27B is a cross-sectional view of the line beam source shown in FIG.22A taken along line B-B.

FIG. 27C is a diagram showing the moving direction of the line beamsource relative to the multilayer stack 100.

FIG. 28A is a diagram schematically showing the upper surface of a linebeam source 214 which includes a plurality of columns of light emittingdiode devices arrayed in Y-axis direction.

FIG. 28B is a cross-sectional view of the line beam source shown in FIG.28A taken along line B-B.

FIG. 28C is a diagram showing the moving direction of the line beamsource relative to the multilayer stack.

FIG. 28D is a plan view schematically showing irradiation regions theline beam source of FIG. 28A is forming.

FIG. 28E is a plan view showing an example of irradiation regions formedby temporarily modulating the electric current flowing through each ofthe light emitting diode devices during scanning by the line beamsource.

FIG. 29 is a top view schematically showing an example of thesurface-emission light source in which a large number of light emittingdiode devices are arrayed in a matrix.

FIG. 30 is a top view schematically showing another example of thesurface-emission light source in which a large number of light emittingdiode devices are arrayed in a matrix.

DESCRIPTION OF EMBODIMENTS

An embodiment of a method and apparatus for producing a flexiblelight-emitting device of the present disclosure is described withreference to the drawings. Examples of the “light-emitting device”include displays and illumination devices. In the following description,unnecessarily detailed description will be omitted. For example,detailed description of well-known matter and repetitive description ofsubstantially identical elements will be omitted. This is for thepurpose of avoiding the following description from being unnecessarilyredundant and assisting those skilled in the art to easily understandthe description. The present inventor provides the attached drawings andthe following description for the purpose of assisting those skilled inthe art to fully understand the present disclosure. Providing thesedrawings and description does not intend to limit the subject matterrecited in the claims.

<Multilayer Stack>

See FIG. 1A and FIG. 1B. In a flexible light-emitting device productionmethod of the present embodiment, firstly, a multilayer stack 100illustrated in FIG. 1A and FIG. 1B is provided. FIG. 1A is a plan viewof the multilayer stack 100. FIG. 1B is a cross-sectional view of themultilayer stack 100 taken along line B-B of FIG. 1A. In FIG. 1A andFIG. 1B, an XYZ coordinate system with X-axis, Y-axis and Z-axis, whichare perpendicular to one another, is shown for reference.

The multilayer stack 100 includes a glass base (motherboard or carrier)10, a plurality of functional layer regions 20 each including a TFTlayer 20A and a light-emitting device layer 20B, a synthetic resin film(hereinafter, simply referred to as “plastic film”) 30 provided betweenthe glass base 10 and the plurality of functional layer regions 20 andbound to the glass base 10, and a protection sheet 50 covering theplurality of functional layer regions 20. The multilayer stack 100further includes a gas barrier film 40 provided between the plurality offunctional layer regions 20 and the protection sheet 50 so as to coverthe entirety of the functional layer regions 20. The multilayer stack100 may include another unshown layer, such as a buffer layer.

In the present embodiment, the light-emitting device layer 20B includes,for example, a plurality of OLED devices which are two-dimensionallyarrayed. In the present disclosure, the “light-emitting device layer”refers to a two-dimensional array of light-emitting devices. Each of thelight-emitting devices is not limited to an OLED device but may be amicro LED device. In the present embodiment, a typical example of theflexible light-emitting device is a “flexible display” but may be a“flexible illumination device”.

The first surface 100 a of the multilayer stack 100 is defined by theglass base 10. The second surface 100 b of the multilayer stack 100 isdefined by the protection sheet 50. The glass base 10 and the protectionsheet 50 are materials temporarily used in the production process butare not constituents of a final flexible light-emitting device.

The plastic film 30 shown in the drawings includes a plurality offlexible substrate regions 30 d respectively supporting the plurality offunctional layer regions 20, and an intermediate region 30 i surroundingeach of the flexible substrate regions 30 d. The flexible substrateregions 30 d and the intermediate region 30 i are merely differentportions of a single continuous plastic film 30 and do not need to bephysically distinguished. In other words, regions of the plastic film 30lying immediately under respective ones of the functional layer regions20 are the flexible substrate regions 30 d, and the other region of theplastic film 30 is the intermediate region 30 i.

Each of the plurality of functional layer regions 20 is a constituent ofa final flexible light-emitting device (e.g., display panel). In otherwords, the multilayer stack 100 has such a structure that a plurality offlexible light-emitting devices which are not yet divided from oneanother are supported by a single glass base 10. Each of the functionallayer regions 20 has such a shape that, for example, the thickness (sizein Z-axis direction) is several tens of micrometers, the length (size inX-axis direction) is about 12 cm, and the width (size in Y-axisdirection) is about 7 cm. These sizes can be set to arbitrary valuesaccording to the required largeness of the display screen or emissionsurface region.

Next, a configuration example of the flexible substrate regions 30 d andthe intermediate region 30 i of the present embodiment is described inmore detail with reference to FIG. 1C. FIG. 1C is a plan view showing anexample of the layout of the flexible substrate regions 30 d and theintermediate region 30 i of the plastic film 30 of the presentembodiment.

In the example illustrated in the drawing, the shape of each of theflexible substrate regions 30 d includes a cutout 30U, protrusions 30V,and curved contour portions 30W. The shape of the flexible substrateregions 30 d is conformable to the shape of the flexible light-emittingdevices shown in FIG. 1A. In the present embodiment, the flexiblelight-emitting devices have a shape different from a simple rectangle.For example, this shape is conformable to the design of an electronicdevice to which a narrow-frame flexible light-emitting device is mountedas a display device, such as smartphone, tablet computer, and televisionset. More specifically, in addition to the display device, parts, suchas camera, loudspeaker, and physical switch, can be mounted to such anelectronic device. The cutout 30U of the flexible substrate regions 30 dshown in FIG. 1C can be provided in a region in which such parts are tobe placed.

The plurality of flexible substrate regions 30 d are two-dimensionallyarrayed in rows and columns according to the arrangement ofcorresponding flexible light-emitting devices. The intermediate region30 i consists of a plurality of stripes perpendicular to one another andforms a grid pattern. The stripes can include large-width portions andnarrow-width portions which accord with the recesses and protrusions ofthe flexible substrate regions 30 d. In the present embodiment, thewidth of each stripe is, for example, about 1-10 mm. The flexiblesubstrate region 30 d of the plastic film 30 functions as the “flexiblesubstrate” in each flexible light-emitting device which is in the formof a final product. Meanwhile, the intermediate region 30 i of theplastic film 30 is not a constituent of the final product.

In an embodiment of the present disclosure, the configuration of themultilayer stack 100 is not limited to the example illustrated in thedrawings. The number of functional layer regions 20 (the number oflight-emitting devices) supported by a single glass base 10 does notneed to be plural but may be singular. If the number of functional layerregions 20 is singular, the intermediate region 30 i of the plastic film30 forms a simple frame pattern surrounding a single functional layerregion 20.

FIG. 1D is a plan view showing a configuration example of the plasticfilm 30 where the number of light-emitting devices supported by a singleglass base 10 is one. In this example, the shape of the flexiblesubstrate region 30 d has a cutout 30U and a protrusion 30V. The shapeof this flexible substrate region 30 d is conformable to the shape of aflexible light-emitting device which can be used for a large-sizedtelevision set or monitor. The cutout 30U of the flexible substrateregion 30 d can be provided in a region in which parts, such as camera,loudspeaker, and physical switch, are to be placed. In this example, asingle flexible light-emitting device can be formed on a glass base 10which has the size of, for example, 1.5 m×0.9 m.

The size or proportion of each component illustrated in respectivedrawings is determined from the viewpoint of understandability. Theactual size or proportion is not necessarily reflected in the drawings.

The multilayer stack 100 which can be used in the production method ofthe present disclosure is not limited to the example illustrated in FIG.1A and FIG. 1B. FIG. 1E and FIG. 1F are cross-sectional views showingother examples of the multilayer stack 100. In the example illustratedFIG. 1E, the protection sheet 50 covers the entirety of the plastic film30 and extends outward beyond the plastic film 30. In the exampleillustrated FIG. 1F, the protection sheet 50 covers the entirety of theplastic film 30 and extends outward beyond the glass base 10. As will bedescribed later, after the glass base 10 is separated from themultilayer stack 100, the multilayer stack 100 is a thin flexiblesheet-like structure which has no rigidity. The protection sheet 50serves to protect the functional layer regions 20 from impact andabrasion when the functional layer regions 20 collide with or come intocontact with external apparatuses or instruments in the step ofdelaminating the glass base 10 and the steps after the delaminating.Since the protection sheet 50 is peeled off from the multilayer stack100 in the end, a typical example of the protection sheet 50 has alaminate structure which includes an adhesive layer of a relativelysmall adhesive force (a layer of an applied mold-releasing agent) overits surface. The more detailed description of the multilayer stack 100will be described later.

<Dividing of Light-Emitting Devices>

According to the flexible light-emitting device production method of thepresent embodiment, after the step of providing the above-describedmultilayer stack 100, the step of dividing an intermediate region 30 iand respective ones of a plurality of flexible substrate regions 30 d ofthe plastic film 30 from one another is carried out.

FIG. 2 is a cross-sectional view schematically showing the positions fordividing the intermediate region 30 i and respective ones of theplurality of flexible substrate regions 30 d of the plastic film 30 fromone another. The positions of irradiation extend along the periphery ofeach of the flexible substrate regions 30 d. In FIG. 2, the positionsindicated by arrows are irradiated with a laser beam for cutting. Partof the multilayer stack 100 exclusive of the glass base 10 is cut into aplurality of light-emitting devices (e.g., display panels) 1000 and theremaining unnecessary portions. By cutting, a gap of several tens ofmicrometers to several hundreds of micrometers is formed between each ofthe light-emitting devices 1000 and a portion surrounding thelight-emitting device 1000. The cutting can also be realized by a cutterwhich has a fixed blade or a rotary blade instead of the laser beamirradiation. Since the periphery of the flexible substrate regions 30 dhas complicated recesses and protrusions and curves as shown in FIG. 1C,the cutting is desirably realized by the laser beam irradiation. Afterthe cutting, the light-emitting devices 1000 and the remainingunnecessary portions remain bound to the glass base 10.

When the cutting is realized by a laser beam, the wavelength of thelaser beam may be in any of the infrared, visible and ultraviolet bands.From the viewpoint of reducing the effect of the cutting on the glassbase 10, the laser beam desirably has a wavelength in the range of greento ultraviolet. For example, when a Nd:YAG laser apparatus is used, thecutting can be carried out using a second harmonic wave (wavelength: 532nm) or a third harmonic wave (wavelength: 343 nm or 355 nm). In such acase, the laser power is adjusted to 1 to 3 watts, and the scanning rateis set to about 500 mm per second, so that the multilayer structuresupported by the glass base 10 can be cut (divided) into Light-emittingdevices and unnecessary portions without damaging the glass base 10.

According to the embodiment of the present disclosure, the timing of theabove-described cutting is earlier than in the prior art. Since thecutting is carried out while the plastic film 30 is bound to the glassbase 10, alignment for the cutting can be made with high precision andaccuracy even if the gap between adjoining light-emitting devices 1000is narrow. Thus, the gap between adjoining light-emitting devices 1000can be shortened, and accordingly, useless portions which areunnecessary for a final product can be reduced. In the prior art, afterthe delaminating from the glass base 10, a polarizer, a heat radiationsheet, and/or an electromagnetic shield can be adhered to the plasticfilm 30 so as to cover the entirety of the surface (delaminated surface)of the plastic film 30. In such a case, the polarizer, the heatradiation sheet, and/or the electromagnetic shield are also divided bycutting into portions covering the light-emitting devices 1000 and theremaining unnecessary portions. The unnecessary portions are disposed ofas waste. On the other hand, according to the production method of thepresent disclosure, production of such waste can be suppressed as willbe described later.

<Lift-Off Light Irradiation>

After the intermediate region 30 i and respective ones of the pluralityof flexible substrate regions 30 d of the plastic film 30 are dividedfrom one another, the step of irradiating the interface between theflexible substrate regions 30 d of the plastic film 30 and the glassbase 10 with lift-off light is carried out using a lift-off lightirradiation unit.

FIG. 3A schematically shows a state immediately before the stage 210supports the multilayer stack 100. In the present embodiment, the stage210 is a chuck stage which has a large number of pores in the surfacefor suction. The multilayer stack 100 is arranged such that the secondsurface 100 b of the multilayer stack 100 faces the surface 210S of thestage 210, and is supported by the stage 210.

FIG. 3B schematically shows a state where the stage 210 supports themultilayer stack 100. The arrangement of the stage 210 and themultilayer stack 100 is not limited to the example illustrated in thedrawing. For example, the multilayer stack 100 may be placed upside downsuch that the stage 210 is present under the multilayer stack 100.

In the example illustrated in FIG. 3B, the multilayer stack 100 is incontact with the surface 210S of the stage 210, and the stage 210 holdsthe multilayer stack 100 by suction.

Then, as shown in FIG. 3C, the interface between the plastic film 30 andthe glass base 10 is irradiated with lift-off light 216. FIG. 3Cschematically illustrates irradiation of the interface between the glassbase 10 and the plastic film 30 of the multilayer stack 100 with thelift-off light 216 in the shape of a line extending in a directionvertical to the sheet of the drawing. A part of the plastic film 30 atthe interface between the glass base 10 and the plastic film 30 absorbsthe lift-off light 216 and decomposes (disappears). By scanning theabove-described interface with the lift-off light 216, the degree ofbinding of the plastic film 30 to the glass base 10 is reduced. Thewavelength of the lift-off light 216 is typically in the ultravioletband. The wavelength of the lift-off light 216 is selected such that thelift-off light 216 is hardly absorbed by the glass base 10 but isabsorbed by the plastic film 30 as much as possible. The lightabsorption by the glass base 10 is, for example, about 10% in thewavelength range of 343-355 nm but can increase to 30-60% at 308 nm.

Hereinafter, lift-off light irradiation according to the presentembodiment is described in detail.

<Lift-Off Light Irradiation Unit 1>

In the present embodiment, the lift-off light irradiation unit includesa line beam source for emitting lift-off light 216. The line beam sourceincludes a laser apparatus and a plurality of arranged laser lightsources. In the present embodiment, a typical example of the laser lightsources is a semiconductor laser device (laser diode, also referred toas “LD”). In contrast, a typical example of a conventional lift-offlight irradiation unit is a combination of a gas laser apparatus such asexcimer laser or a solid state laser apparatus such as YAG laser and anoptical system consisting of lenses and prisms for reshaping laser lightin the form of a spot beam emitted from the laser apparatus into a linebeam. In the present disclosure, the lift-off light irradiation unit issimply referred to as “delaminating apparatus”. Note that, inconventional delaminating apparatuses, if the line length of a line beamto be produced is 1 m or more, the optical system for reshaping thelaser light is too big to construct and, accordingly, deterioration ofthe quality (uniformity) of the line beam is inevitable. Thus, thelongest possible line beam has a length corresponding to the G6Hsubstrate size (the shorter side of a 1800 mm×750 mm rectangle), i.e., abeam length up to about 750 mm.

FIG. 4 is a perspective view schematically showing irradiation of themultilayer stack 100 with a line beam (lift-off light 216) emitted fromthe line beam source 214 of a delaminating apparatus 220 of the presentembodiment. For the sake of understandability, the stage 210, themultilayer stack 100 and the line beam source 214 are shown as beingspaced away from one another in the Z-axis direction of the drawing.During irradiation with the lift-off light 216, the second surface 100 bof the multilayer stack 100 is in contact with the stage 210. When aplurality of thus-arrayed laser light sources are used, the line lengthof the lift-off light in the shape of a line beam can easily be 1 m ormore, and the delaminating apparatus is applicable to GB-size substrates(2400 mm×2200 mm) or huge substrates of still larger sizes, to whichconventional delaminating apparatuses are not applicable.

The delaminating apparatus 220 illustrated in FIG. 4 includes atransporting device 230 for moving the line beam source 214 such thatthe irradiation position of the line beam on the multilayer stack 100moves in a direction transverse to the line beam (scanning direction).The transporting device 230 illustrated in the drawing includes asupporting base 270 and a guide rail 246 for guiding the movement of theline beam source 214. The transporting device 230 includes an actuatorsuch as, for example, a motor and is capable of moving the line beamsource 214. The motor may be a rotating electric machine, such as DCmotor, three-phase AC motor, stepping motor, or may be a linear motor oran ultrasonic motor. When an ultrasonic motor is used, highly-accuratepositioning is possible as compared with the other types of motors.Further, the ultrasonic motor provides large holding power when it isnot moving, and can hold without supply of electric power. Therefore,the heat generation is small when it is not moving.

Next, see FIG. 5. FIG. 5 is a block diagram schematically showing theflow of signals, data and instructions in the delaminating apparatus220.

The controller 260 is typically a computer. A part or the entirety ofthe controller 260 can be a general-purpose or special-purpose computersystem. The computer system includes an OS (operating system) and, whennecessary, hardware devices such as peripheral devices. The controller260 is connected with a memory 274 which is a computer-readable storagemedium. In the memory 274, a program is stored which defines theoperation of the delaminating apparatus 220.

In FIG. 5, for the sake of simplicity, a single memory unit is shown.However, the actual memory 274 can consist of a plurality of storagedevices of an identical type or different types. A part of the memory274 may be a nonvolatile memory while the other part may be a randomaccess memory. A part or the entirety of the memory 274 may be aneasily-detachable optical disc or solid-state recording element or maybe a cloud-type storage on a net multilayer stack.

The controller 260 is connected with a sensor 276, such as temperaturesensor and image sensor. Such a sensor 276 enables detection of theirradiation position of the line beam on the multilayer stack 100 ormonitoring of a physical or chemical change in the multilayer stack 100which can be caused by irradiation.

The controller 260 follows the program stored in the memory 274 andissues appropriate instructions to a laser driving circuit (LD drivingcircuit) 280 and a transporting device driving circuit 290, whennecessary, based on the output of the sensor 276. The LD driving circuit280 adjusts the irradiation intensity of the line beam emitted from theline beam source 214 according to the instruction from the controller260. The transporting device driving circuit 290 adjusts the operationof the transporting device 230 according to the instruction from thecontroller 260.

The transporting device driving circuit 290 controls, for example, therotation angle and the rotation speed of the motor in order to adjustthe mutual positional relationship between the line beam source 214 andthe stage 210. In this example, for the sake of simplicity, the linebeam source 214 moves in the X-axis direction while the stage 210 isfixed, although the delaminating apparatus of the present embodiment isnot limited to this example. The stage 210 may move while the line beamsource 214 is fixed. Alternatively, both the stage 210 and the line beamsource 214 may move in an identical direction or in differentdirections. When the stage 210 moves while the stage 210 supports aheavy-weight multilayer stack 100, a bearing such as, for example, airslider can be used.

The line beam source 214 includes a plurality of arranged semiconductorlaser devices. Each of the semiconductor laser devices is connected witha laser diode (LD) driving circuit 280. The LD driving circuit 280receives an electric signal from the above-described photodiode formonitoring and adjusts the optical power of the semiconductor laserdevice to a predetermined level.

<Semiconductor Laser Device>

FIG. 6 is a perspective view schematically showing a basic configurationof a semiconductor laser device which can be used in the line beamsource 214. The semiconductor laser device 300 shown in FIG. 6 includesa semiconductor multilayer stack 322 which has a facet 326 a. The facet326 a includes an emission region (emitter) 324 from which laser lightis to be emitted. In this example, the semiconductor multilayer stack322 is supported on a semiconductor substrate 320 and includes a p-typecladding layer 322 a, an active layer 322 b, and an n-type claddinglayer 322 c. On the upper surface 326 b of the semiconductor multilayerstack 322, a p-side electrode 312 in the shape of a stripe is provided.On the rear surface of the semiconductor substrate 320, an n-sideelectrode 316 is provided. When an electric current which is greaterthan a threshold flows through a predetermined region of the activelayer 322 b from the p-side electrode 312 to the n-side electrode 316,laser oscillation occurs. The facet 326 a of the semiconductormultilayer stack 322 is covered with an unshown reflective film. Laserlight is emitted from the emission region 324 via the reflective film.

In general, a size in the Y-axis direction of the emission region 324,Ey, is smaller than a size in the X-axis direction of the emissionregion 324, Ex. Thus, laser light emitted from the emission region 324diverges in the Y-axis direction due to a diffraction effect. Accordingto the embodiment of the present disclosure, formation of a line beamcan be realized by utilizing this diffraction effect. Note that anoptical element, such as lens, diffraction element, slit, may beprovided over the front surface of the emission region 324 for beamreshaping of the laser light.

The semiconductor laser device 300 can be made of various semiconductormaterials and can have various configurations and sizes according to theoscillation wavelength and the optical power. When the laser light isrequired to have a wavelength in the ultraviolet region (e.g., 300-350nm), the semiconductor multilayer stack 322 of the semiconductor laserdevice 300 can be suitably made of a nitride semiconductor, such asAlGaN-based semiconductor or InAlGaN-based semiconductor. Theoscillation wavelength of the semiconductor laser device 300 can be setwithin the range of, for example, 200 nm to 350 nm. A ridge stripe maybe provided in the p-type cladding layer 322 a such that lightconfinement in the horizontal transverse direction is realized. Theactive layer 322 b may include a single or a plurality of quantum wellstructures. The semiconductor multilayer stack 322 may include othersemiconductor layers, such as a light guiding layer, a buffer layer, anda contact layer. When the substrate 320 is a sapphire substrate, then-side electrode 316 is provided on a side of the substrate 320 on whichthe p-side electrode 312 is provided.

The configuration shown in FIG. 6 is merely a typical example of theconfiguration of the semiconductor laser device 300 and is simplifiedfor the sake of simple description. This simplified configurationexample does not limit embodiments of the present disclosure. The linebeam can also be formed using a surface-emission type semiconductorlaser device. Note that, in the other drawings, constituents such as then-side electrode 316 will be omitted for the sake of simplicity.

<Configuration Example of Line Beam Source>

See FIG. 7A. The line beam source 214 includes a plurality ofsemiconductor laser devices 300 and a plurality of supports 214Asupporting the semiconductor laser devices 300. The semiconductor laserdevices 300 and the supports 214A are held in a casing 214B. Thesupports 214A may be suitably made of a good conductor of high thermalconductivity, e.g., a metal such as copper or a ceramic material such asaluminum nitride. The casing 214B is closed with, for example, anunshown light-transmitting cover, whereby the inside of the casing 214Ecan be shielded from the atmosphere. The inside of the casing 214B isfilled with, for example, a gas which is inert with the semiconductorlaser devices 300. Each of the semiconductor laser devices 300 issupplied with electric power via an unshown wire (metal wire, metalribbon, or the like). To suppress increase of the temperature of thesemiconductor laser devices 300 during operation, a thermoelectriccooling device (not shown) such as Peltier device may be provided nearthe semiconductor laser devices 300. The supports 214A may include aninternal channel for water cooling and fins for air cooling.

In each of the semiconductor laser devices 300, an unshown photodiode isprovided near a facet 326 c of the semiconductor laser device 300 whichis opposite to the emission-side facet 326 a. This facet 326 c iscovered with a reflective film which has a relatively-high reflectance.However, part of laser light oscillating inside the semiconductor laserdevice 300 leaks out from the facet 326 c. This laser light leakage isdetected by the photodiode, whereby the intensity of laser light emittedfrom the facet 326 a can be monitored. The output of the photodiode isused for power control as previously described.

In the example of FIG. 7A, eleven semiconductor laser devices 300 arearranged along an identical line which is parallel to the Y-axis. Thenumber of semiconductor laser devices 300 is not limited to this examplebut may be not more than ten or may be not less than twelve. To form along line beam for irradiating a large-area region or to modulate thespatial distribution of the irradiation intensity at high resolution,more than 50 or more than 100 semiconductor laser devices 300 can bearranged on the same line. Each of the semiconductor laser devices 300can have the same configuration as that of the semiconductor laserdevice 300 of FIG. 6. Laser light (lift-off light 216) emitted from theemission regions 324 of respective ones of the semiconductor laserdevices 300 diverge in parallel to the same line so as to form a linebeam.

In FIG. 7A, a rectangular scanned surface SC which is parallel to the XYplane and an irradiation region 218 which is formed by laser light(lift-off light 216) on the scanned surface SC are schematically shown.The scanned surface SC is equivalent to the interface between theplastic film 30 and the glass base 10 in the multilayer stack 100.

For the sake of reference, FIG. 7A shows the X-axis directiondistribution and the Y-axis direction distribution of the irradiationintensity IS in the irradiation region 218 at a certain time. The X-axisdirection distribution of the irradiation intensity IS is narrow andunimodal. Meanwhile, the Y-axis direction distribution of theirradiation intensity IS has eleven peaks because laser light emittedfrom respective ones of the eleven semiconductor laser devices 300overlap one another and extend in the shape of a line.

As previously described, laser light emitted from each of thesemiconductor laser devices 300 has a tendency to diverge in apredetermined direction (in this example, Y-axis direction) due to adiffraction effect. This characteristic is suitable to formation of aline beam extending in the Y-axis direction. Meanwhile, an opticalelement such as cylindrical lens may be used in order to suppress thedivergence in the X-axis direction such that the irradiation energy inevery second per unit area (irradiation intensity expressed injoule/cm²) is increased. When such an optical element is used to focusthe laser light in the X-axis direction, the width (the size in theX-axis direction) of the irradiation region 218 on the scanned surfaceSC can be narrowed to, for example, about 0.2 mm or smaller.

From the viewpoint of increasing the irradiation intensity of the linebeam, it is preferred to decrease the arrangement pitch of thesemiconductor laser devices 300 such that the number density of thesemiconductor laser devices 300 is increased. For example, 100 or moresemiconductor laser devices 300 may be arranged in a straight line atintervals of 1 mm to 5 mm (arrangement pitch: the distance between thecenters of adjoining light sources). When the semiconductor laserdevices 300 are arranged at such a high density and the distance fromthe semiconductor laser devices 300 to the scanned surface SC is forexample 10 mm, the irradiation intensity can be modulated at a highspatial resolution of, for example, 1 mm to 5 mm. To achieve a highspatial resolution, an optical element which can prevent the crosssection of laser light emitted from each of the semiconductor laserdevices 300 from diverging (an optical system for collimation orconvergence) may be provided on the optical path of the laser light.

Next, see FIG. 7B. FIG. 7B shows the line beam source 214 translatedfrom the position shown in FIG. 7A in the positive direction of theX-axis. The irradiation region 218 is also translated according to themovement of the line beam source 214. In the state of FIG. 7B, the powerof each of the semiconductor laser devices 300 is lower than that in thestate of FIG. 7A. It is not necessary to increase or decrease the powersof respective ones of the semiconductor laser devices 300 at the sametiming. In other words, not only the X-axis direction distribution ofthe irradiation intensity IS but also the Y-axis direction distributioncan be variously changed during the scanning with the line beam.

By using the thus-arranged plurality of semiconductor laser devices 300,the power of the semiconductor laser devices 300 can be temporallyand/or spatially modulated according to the position of the irradiationregion 218. Thus, the distribution of the irradiation intensity acrossthe scanned surface SC can be controlled.

FIG. 8 is a perspective view schematically showing another configurationexample of the line beam source 214 that includes a plurality ofsemiconductor laser devices 300. In this example, the semiconductorlaser devices 300 arranged in two rows have a stagger pattern (staggeredarrangement). By reducing the distance between the centers of the tworows, a single line beam can be formed in total. When the orientation ofthe semiconductor laser devices 300 is adjusted such that the opticalaxes of the semiconductor laser devices 300 included in the first rowand the optical axes of the semiconductor laser devices 300 included inthe second row intersect with each other on the multilayer stack 100,substantially a single line beam can be formed.

According to the “line beam source” of the embodiment of the presentdisclosure, the irradiation region of the lift-off light does not needto be a single line. The irradiation region only needs to becontinuously or discontinuously distributed in a direction transverse tothe scanning direction. In other words, it is only necessary that theline beam source includes a plurality of light sources arranged along aline. The number of such lines is not limited to being singular but maybe two or more.

Next, see FIG. 9. FIG. 9 is a diagram schematically showing an exampleof the distribution in the Y-axis direction of the irradiation intensityof the lift-off light 216. In the graph of FIG. 9, the horizontal axisrepresents the Y-axis coordinate of the irradiation region, and thevertical axis represents the irradiation intensity. The irradiationintensity is expressed by the energy density per unit area (e.g.,[mJ/cm²]). In the graph of FIG. 9, specific numbers of the irradiationintensity are not shown. The irradiation intensity refers to a value inthe range of, for example, not less than 0 mJ/cm² and not more than 500mJ/cm².

A curve shown by a broken line in the graph of FIG. 9 represents thedistribution in the Y-axis direction of the irradiation intensity, I(Y).The Y-axis direction distribution I(Y) of the irradiation intensity isdefined by overlapping of the light intensity distributions of laserlight emitted from the plurality of semiconductor laser devices 300 ofthe line beam source 214 (e.g., FIG. 7A). The light intensitydistribution of the laser light emitted from each of the semiconductorlaser devices 300 can be reshaped using an optical element such as lens.The light intensity distribution shown in the drawing is merelyexemplary. In FIG. 9, a straight dot-chain line represents thresholdlevel Th of the irradiation intensity which is necessary fordelamination. Threshold level Th is, for example, 250-300 mJ/cm². In aregion irradiated with lift-off light at an irradiation intensity lowerthan this threshold level Th, the amount of lift-off light absorbed bythe plastic film 30 is insufficient. Therefore, the plastic film 30 inthat region remains bound, without being delaminated from the glass base10.

In FIG. 9, a cross section of the multilayer stack 100 which is parallelto the YZ plane is shown above the graph for reference. The glass base10 extends from position Y0 to position Y5. The light-emitting device1000 on the left-hand side resides in the region extending from positionY1 to position Y2. The light-emitting device 1000 on the right-hand sideresides in the region extending from position Y3 to position Y4. Inother words, the flexible substrate regions 30 d of the plastic film 30correspond to the region extending from position Y1 to position Y2 andthe region extending from position Y3 to position Y4. Meanwhile, theintermediate region 30 i of the plastic film 30 corresponds to theregion extending from position Y0 to position Y1, the region extendingfrom position Y2 to position Y3, and the region extending from positionY4 to position Y5.

In the example of FIG. 9, the irradiation intensity distribution I(Y) ofthe lift-off light is higher than threshold level Th in the regionextending from position Y1 to position Y2 and the region extending fromposition Y3 to position Y4. In other words, the interface between theflexible substrate regions 30 d of the plastic film 30 and the glassbase 10 is irradiated with lift-off light whose irradiation intensityexceeds threshold level Th. Meanwhile, each of the region extending fromposition Y0 to position Y1, the region extending from position Y2 toposition Y3, and the region extending from position Y4 to position Y5includes a portion in which the irradiation intensity distribution I(Y)of the lift-off light is lower than threshold level Th.

The smallest value of the irradiation intensity distribution I(Y) of thelift-off light during the scanning is typically 0 mJ/cm² but may begreater than 0 mJ/cm² so long as it is lower than threshold level Th.

When an amorphous semiconductor is heated and crystallized byirradiation with laser light in the shape of a line beam, theirradiation intensity distribution is desired to be uniform in order toachieve uniform crystallinity. On the other hand, when the delaminationin the present embodiment is carried out, the irradiation intensity ofthe line beam does not need to be uniform so long as the irradiationintensity of the lift-off light at the interface which needsdelamination exceeds threshold level Th.

In the example of FIG. 9, the irradiation intensity distribution I(Y) ofthe lift-off light has many peaks, although the embodiment of thepresent disclosure is not limited to such an example. For example, asillustrated in FIG. 10, part of the irradiation intensity distributionI(Y) of the lift-off light may be linear. In the example of FIG. 10, thelight intensity distribution of laser light emitted from each of thesemiconductor laser devices 300 of the line beam source 214 (e.g., FIG.7A) is flat at the center of its optical axis, i.e., “top hat” type. Ifthe irradiation intensity of the lift-off light at the interface whichneeds delamination exceeds threshold level Th as described above, theirradiation intensity of the line beam does not need to be uniform.Thus, the optical powers of the plurality of semiconductor laser devices300 may be different from one another.

According to the present embodiment, in the irradiation intensitydistribution I(Y), the irradiation intensity of laser light for theinterface between the intermediate region 30 i of the plastic film 30and the glass base 10 is lower than the irradiation intensity of laserlight for the interface between the flexible substrate regions 30 d ofthe plastic film 30 and the glass base 10.

FIG. 11 shows an example of the Y-axis direction distribution I(Y) in across section which is different from the Y-axis direction distributionI(Y) shown in FIG. 9. This cross section extends across the protrusions30V and the cutout 30U of the flexible substrate regions 30 d shown inFIG. 1C.

In the cross section shown in FIG. 11, the center of each of twolight-emitting devices 1000 includes a portion which is to be bound tothe glass base 10, without being delaminated together with theintermediate region 30 i of the plastic film 30 from the glass base 10.

In the example of FIG. 11, the power of some of the semiconductor laserdevices that are constituents of the line beam source 214 is decreased,whereby the Y-axis direction distribution I(Y) is made locally lowerthan threshold level Th at the interface between the intermediate region30 i of the plastic film 30 and the glass base 10. Of a portion in whichthe irradiation intensity is lower than threshold level Th, a partcorresponding to the cutout 30U of the flexible substrate region 30 dforms a “large-width portion” in the striped “low irradiation region”.

FIG. 12 shows another example of the Y-axis direction distribution I(Y)in the same cross section as that of FIG. 11. The Y-axis directiondistribution I(Y) of FIG. 12 can be realized by a line beam source 214which includes 27 or more aligned semiconductor laser devices. In thisexample, laser light emitted from each semiconductor laser device canrealize a Y-axis direction distribution I(Y) which changes at a higherspatial resolution than in the example of FIG. 11. Note that at theinterface between the intermediate region 30 i of the plastic film 30and the glass base 10, the irradiation intensity may be zero.

According to the embodiment of the present disclosure, the line beamsource 214 includes a plurality of laser light sources, and therefore,the irradiation intensity in the line beam can be spatially andtemporally modulated by adjusting the power of each laser light source.Thus, a spatial distribution of the irradiation intensity which accordswith the shape, size and arrangement of the light-emitting devices 1000included in the multilayer stack 100 can be easily realized. Morespecifically, the spatial distribution of the irradiation intensity inthe line beam is temporally changed during scanning such that theflexible substrate regions 30 d which have a shape such as shown in, forexample, FIG. 1C or FIG. 1D can be irradiated with lift-off light at anirradiation intensity which is necessary for delamination while theintermediate region 30 i of the plastic film 30 can be irradiated withlift-off light at an irradiation intensity which would not causedelamination. If the type or design of the multilayer stack 100 to beproduced is changed, the distribution of the irradiation intensity canbe flexibly modulated.

The region in which the irradiation intensity of the lift-off light islower than a level necessary for delamination does not need to includethe entirety of the intermediate region 30 i of the plastic film 30. Theentirety of the unnecessary portions of the multilayer stack 100 can beleft on the glass base 10 so long as part of the intermediate region 30i of the plastic film 30 is bound to the glass base 10. According to theembodiment of the present disclosure, the unnecessary portions of themultilayer stack 100 can be left on the glass base 10 in a wide rangewhich accords with its shape.

A typical example of the laser light source is a semiconductor laserdevice, although the embodiment of the present disclosure is not limitedto this example. When a semiconductor laser device is used, a smallsize, lightweight line beam source can advantageously be realized.However, when the multilayer stack 100 is moved during the scanning,each of a plurality of laser light sources may be a large laserapparatus as compared with the semiconductor laser device. When theoscillation wavelength of the laser light source is out of a rangesuitable for delamination of the plastic film, the laser light may beconverted to a harmonic wave using a wavelength converter.

Next, see FIG. 13. FIG. 13 is a diagram schematically showing an exampleof the distribution in the X-axis direction (scanning direction) of theirradiation intensity of the lift-off light 216. In the graph of FIG.13, the horizontal axis represents the X-axis coordinate of theirradiation position, and the vertical axis represents the irradiationintensity. In the graph of FIG. 13, the solid line represents the X-axisdirection distribution I(X) of the irradiation intensity, and a straightdot-chain line represents threshold level Th of the irradiationintensity which is necessary for delamination.

In FIG. 13, a cross section of the multilayer stack 100 which isparallel to the XZ plane is shown above the graph for reference. Thiscross section is perpendicular to the cross section of FIG. 9. The glassbase 10 extends from position X0 to position X5. The light-emittingdevice 1000 on the left-hand side in the drawing resides in the regionextending from position X1 to position X2. The light-emitting device1000 on the right-hand side resides in the region extending fromposition X3 to position X4. In other words, the flexible substrateregions 30 d of the plastic film 30 correspond to the region extendingfrom position X1 to position X2 and the region extending from positionX3 to position X4. Meanwhile, the intermediate region 30 i of theplastic film 30 corresponds to the region extending from position X0 toposition X1 (width: W1), the region extending from position X2 toposition X3 (width: W3), and the region extending from position X4 toposition X5 (width: W2). The intermediate region 30 i at the left edgeof the plastic film 30 in FIG. 13 (width: W1) includes a region in whichthe irradiation intensity is lower than threshold level Th (width: S1).Meanwhile, the intermediate region 30 i at the right edge of the plasticfilm 30 in FIG. 13 (width: W2) includes a region in which theirradiation intensity is lower than threshold level Th (width: S2).Here, W1>S1 and W2>S2 hold. It is preferred that width S1 is not lessthan 50% of width W1 and width S2 is not less than 50% of width W2.

The X-axis direction distribution I(X) of the irradiation intensityrepresents the whole scanning (sum or integral value) of the lift-offlight. For example, while the irradiation position of the lift-off light(the position of the center line of the line beam) moves from positionX0 to position X5, the region extending from position X4 to position X5is not irradiated with the lift-off light. In this period, theirradiation intensity of the lift-off light in the region extending fromposition X4 to position X5 is, as a matter of course, zero.

The line width (the transverse axis dimension, the size in the X-axisdirection) of the lift-off light 216 can be, for example, about 0.2 mm.This dimension defines the largeness of the irradiation region at theinterface between the plastic film 30 and the glass base 10 at a certaintime. The lift-off light 216 can be emitted in the form of a pulsed orcontinuous wave. Irradiation with the pulsed wave can be carried out atthe frequency (the number of shots in one second) of, for example, about200 times per second. When the lift-off light 216 is a pulsed wave, thescanning speed is determined such that two consecutive shots formpartially-overlapping irradiation regions. If, for example, the linewidth (the transverse axis dimension, the size in the X-axis direction)of the lift-off light 216 is 0.2 mm and the irradiation position movesat 20 mm per second in the X-axis direction, a gap can occur betweenneighboring shots so long as the number of shots per second is less than100. Therefore, the number of shots per second needs to exceed 100.

The positioning accuracy of the irradiation position depends on themechanical forwarding accuracy of the line beam source 214. When theline width (the transverse axis dimension, the size in the X-axisdirection) of the lift-off light 216 is, for example, 40 μm, moving theline beam source 214 stepwise at intervals of 20 μm can set the overlapof irradiation regions formed by two consecutive shots to 50%. Movingthe line beam source 214 stepwise at intervals of 30 μm can set theoverlap of irradiation regions formed by two consecutive shots to 75%.By controlling the overlap of irradiation regions, the irradiationintensity can also be changed without modulating the power of the laserlight source.

When the irradiation position of the lift-off light is forwardedstepwise, “stepwise movement of the line beam source 214” and “pulsedirradiation with the lift-off light” can be repeated. In this case,irradiation with the lift-off light can be carried out while movement ofthe line beam source 214 relative to the stage 210 is stopped. Inirradiation of a stationary object with laser light, adjustment of theirradiation intensity to a target value is easier than in irradiation ofa moving object with laser light. For example, the irradiation intensitycan be adjusted by, for example, increasing or decreasing the number ofirradiation pulses or the irradiation duration at a stationary position.According to the embodiment of the present disclosure, a semiconductorlaser device is used for the light source, and therefore,advantageously, the irradiation intensity can be easily controlled byadjusting the oscillation state of the semiconductor laser device.

When the moving speed (scanning speed) of the irradiation position isfixed to a predetermined value, the irradiation intensity can bemodulated by increasing or decreasing the number of shots per second. Onthe contrary, when the number of shots per second is fixed, theirradiation intensity can be modulated by increasing or decreasing themoving speed (scanning speed) of the irradiation position. Theirradiation intensity can also be modulated by changing the otherparameters, e.g., the optical distance from the line beam source 214 tothe multilayer stack 100. Also, a low irradiation region can be formedby providing a mechanical shutter between the line beam source 214 andthe glass base 10 such that this shutter blocks the optical path of thelift-off light.

As seen from FIG. 13, in this example, the irradiation intensity oflift-off light for at least part of the interface between theintermediate region 30 i of the plastic film 30 and the glass base 10 islower than the irradiation intensity of lift-off light for the interfacebetween the flexible substrate regions 30 d of the plastic film 30 andthe glass base 10. The region of this “at least part” may be referred toas “low irradiation region” or “non-delamination region”. In the exampleof FIG. 13, the low irradiation region includes two parallel striperegions extending along the perimeter of the glass base 10 (a region ofwidth S1 and a region of width S2). The two stripe regions can be formedby irradiation with weak lift-off light 216 shown in FIG. 5A and FIG.5D. In these two stripe regions, the irradiation intensity of thelift-off light 216 is lower than threshold level Th, and therefore, theintermediate region 30 i of the plastic film 30 remains bound to theglass base 10.

As previously described with reference to FIG. 9 and FIG. 11, in theembodiment of the present disclosure, the distribution in the Y-axisdirection of the irradiation intensity is changed while the irradiationposition of the lift-off light is moved along the X-axis (duringscanning). Thus, any of the stripe regions which define the “lowirradiation region” can include a large-width portion and/ornarrow-width portion which accords with the intermediate region 30 i ofthe plastic film 30. By thus making the shape and size of the “lowirradiation region” conformable to those of the intermediate region 30 iof the plastic film 30, the degree of adhesion between the intermediateregion 30 i of the plastic film 30 and the glass base 10 can be improvedas a whole. It is not desired that the “low irradiation region” extendsbeyond the intermediate region 30 i of the plastic film 30 into theflexible substrate regions 30 d.

FIG. 14 shows an example where the irradiation intensity is temporarilylower than threshold level Th in the middle of the scanning with thelift-off light 216. Specifically, the irradiation intensity is lowerthan threshold level Th in part of the region extending from position X2to position X3 (width: S3). In this example, the “low irradiationregion” at the interface between the intermediate region 30 i of theplastic film 30 and the glass base 10 includes not only the two striperegions but also a single middle stripe region (width: S3) which isparallel to the two stripe regions. Each of widths S1, S2, S3 of thesestripe regions is, for example, not less than 1 mm and, in a certainexample, not less than 3 mm.

In the examples of FIG. 13 and FIG. 14, two light-emitting devices 1000are arranged in the direction of the X-axis. When N is an integer notless than 3 and N light-emitting devices 1000 are arranged in thedirection of the X-axis, the total number of stripes formed by theintermediate region 30 i lying between two adjoining light-emittingdevices 1000 is N−1. It is not necessary to provide a low irradiationregion in all of the N−1 stripes. Alternatively, a plurality of lowirradiation regions may be provided for an intermediate region 30 iwhich forms a single stripe.

In the examples of FIG. 13 and FIG. 14, the low irradiation region ofwidth S1 and the low irradiation region of width S2 each reach theperimeter of the plastic film 30, although the embodiment of the presentdisclosure is not limited to this example. For example, the lowirradiation region can be in various forms as shown in FIG. 15A and FIG.15B. FIG. 15A and FIG. 15B are diagrams schematically showing stillother examples of the distribution in the X-axis direction of theirradiation intensity of the lift-off light. In these drawings, examplesof the modulation pattern of the irradiation intensity at the interfacebetween the intermediate region 30 i surrounding the light-emittingdevice 1000 on the left-hand side of FIG. 13 and the glass base 10 areshown.

In the example shown in FIG. 15A, the striped low irradiation regions(width: S1) extending along the perimeter of the plastic film 30 do notreach the perimeter of the plastic film 30. The irradiation intensity ofthe lift-off light may exceed threshold level Th before the glass base10 is irradiated with the lift-off light. As in the region extendingfrom position X1 to position X3 shown in FIG. 15A, the irradiationintensity may gradually change. When the irradiation intensity graduallychanges, the width (the size in the scanning direction) of the “lowirradiation region” can be defined as the width of a region in which theirradiation intensity is lower than threshold level Th.

In the example shown in FIG. 15B, the low irradiation region consists ofa plurality of stripes which have a relatively narrow width. When thelift-off light is, for example, pulsed light, such a low irradiationregion can be realized by applying consecutive shots such thatirradiation regions do not overlap each other.

To maintaining at least part of the intermediate region 30 i of theplastic film 30 bound to the glass base 10 by relatively decreasing theirradiation intensity, it is desirable that the irradiation intensity inthe “at least part” is lower than threshold level Th. However, even ifit is not lower than threshold level Th, the intermediate region 30 i islikely to remain on the glass base 10 so long as an irradiationintensity which is lower than the irradiation intensity in a region tobe delaminated is realized. If the difference between the irradiationintensity in a region to be delaminated and the irradiation intensity inthe low irradiation region is not less than 50 mJ/cm², a sufficienteffect is achieved.

In the present embodiment, the lift-off light is a line beam extendingin a direction parallel to the perimeter of the glass base 10 (firstdirection), and the scanning direction is the second direction which isperpendicular to the first direction. However, the first direction andthe second direction do not need to be perpendicular to each other butonly need to be transverse to each other.

In the above-described example, as previously described with referenceto FIG. 4, the position of the line beam source 214 is moved while thestage 210 is fixed, whereby the irradiation position of the lift-offlight is moved (scanning). However, the embodiment of the presentinvention is not limited to this example. Scanning with the lift-offlight may be carried out by moving the stage 210 while the line beamsource 214 is fixed. Alternatively, scanning with the lift-off light maybe carried out by moving both the line beam source 214 and the stage210.

<Lift-Off Light Irradiation Unit 2>

In the above-described embodiment, the plurality of light sourcesincluded in the lift-off light irradiation unit are a plurality ofsemiconductor laser devices, although the lift-off light irradiationunit of the present disclosure is not limited to this example. Thelift-off light may be radiated from an incoherent light source insteadof a coherent light source such as laser light source. In the exampledescribed in the following paragraphs, the interface between the plasticfilm and the glass base is irradiated with lift-off light radiated froma plurality of light emitting diode devices.

As the light source for radiating the lift-off light, light emittingdiode devices are available at a lower cost than semiconductor laserdevices, and designing and operation of the apparatus are easier fromthe viewpoint of eye-safety. Light emitting diode (UV-LED) devices whichare capable of radiating ultraviolet light have the size of, forexample, 3.5 mm (longitudinal)×3.5 mm (transverse)×1.2 mm (thickness).The plurality of light emitting diode devices can be arrayed in a singleline or in a plurality of lines. Also in this case, when a plurality oflight emitting diode devices are arrayed, the delaminating apparatus isapplicable to G8-size substrates (2400 mm×2200 mm) or huge substrates ofstill larger sizes, to which conventional delaminating apparatuses arenot applicable.

The emission intensity of the light-emitting diode device is alsocontrolled by adjusting the magnitude of the driving current as in theabove-described semiconductor laser devices. Therefore, in aone-dimensional or two-dimensional array of light emitting diodedevices, by modulating the driving current flowing through each of thelight emitting diode devices, the irradiation intensity of the lift-offlight can be temporally and/or spatially modulated.

The array pitch of the light emitting diode devices is in the range of,for example, not less than 3 mm and not more than 10 mm. The lightradiated from the light emitting diode devices is incoherent(non-coherent) light, which is different from laser light. Thewavelength of the light radiated from the light emitting diode devicesis in the range of, for example, not less than 300 nm and not more than380 nm. The irradiation energy of the lift-off light radiated from eachof the plurality of arrayed light emitting diode devices is in the rangeof not less than 100 mJ/cm² and not more than 300 mJ/cm².

Light radiated from each of the light emitting diode devices divergesaround the Z-axis direction at the center. This light represents thedistribution (directivity) of the relative radiation intensity whichdepends on the radiation angle θ that is the gradient from the Z-axis.In one example, the relative radiation intensity of the light emittingdiode devices can be about 75% at θ=45°, and about 50% at θ=65°. Thedirectivity of the light emitting diode devices can be adjusted byproviding a lens and/or reflector.

Commercially-available light emitting diode devices are capable ofradiating ultraviolet light at 365 nm with the power of 1450 milliwattson the driving conditions that, for example, the electric voltage is3.85 volts and the electric current is 1000 milliamperes.

An example of a line beam light source in which a plurality of lightemitting diode devices are arrayed is described with reference to FIG.27A, FIG. 27B and FIG. 27C.

FIG. 27A schematically shows the upper surface of a line beam lightsource 214 which includes a plurality of light emitting diode devices400 arrayed in Y-axis direction. FIG. 27B is a cross-sectional view ofthe line beam light source 214 shown in FIG. 27A taken along line B-B.FIG. 27B also shows a multilayer stack 100. FIG. 27C is a diagramshowing the moving direction of the line beam light source 214 relativeto the multilayer stack 100.

As shown in FIG. 27A, the line beam light source 214 can be coupled witha driving circuit 280A. The driving circuit 280A can modulate themagnitude of the electric current flowing through each of the lightemitting diode devices 400. The driving circuit 280A can be coupled witha controller 260. The controller 260 controls the operation of thedriving circuit 280A, thereby temporally and/or spatially modulating theirradiation intensity of the lift-off light radiated from the line beamlight source 214.

In this example, the ultraviolet light radiated from the light emittingdiode devices 400 travels through a cylindrical lens 410 and enters theglass base 10 of the multilayer stack 100 in order to increase theirradiation energy per unit area (irradiation intensity expressed injoule/cm²). Since the ultraviolet light is focused in X-axis direction,the width (the size in X-axis direction) of the irradiation region inthe interface at which delamination is to occur (delamination plane) canbe decreased to, for example, about 0.2 mm or smaller. Since thecylindrical lens 410 does not focus the light in X-axis direction, thesize in Y-axis direction of the irradiation region is not shortened.

The irradiation intensity of the lift-off light can be increased bydecreasing the array pitch of the light emitting diode devices 400 suchthat the number density of the light emitting diode devices 400increases. For example, when each of the light emitting diode devices400 has the above-described size, several tens of light emitting diodedevices 400 or 100 or more light emitting diode devices 400 may bearrayed with the intervals of 3.5 mm to 10 mm (array pitch: the distancebetween the centers of adjoining light sources). When smaller lightemitting diode devices 400 are used, they can be arrayed with theintervals of, for example, 2 mm to 10 mm. The array pitch of the lightemitting diode devices 400 is preferably not more than 5 mm.

When light emitting diode devices 400 of high directivity are arrayed ata high density and the distance from the light emitting diode devices400 to the delamination plane is, for example, 1.5-5 mm, the irradiationintensity can be modulated at the spatial resolution of 2 mm to 10 mmeven without an optical element such as cylindrical lens.

The electric current flowing through each of the light emitting diodedevices is modulated while the line beam light source 214 is movedrelative to the multilayer stack 100 as shown in FIG. 27C. As a result,lift-off light irradiation can be realized in the same way as theembodiment with the use of the line beam light source 214 which includesa plurality of arrayed semiconductor laser devices 300.

To increase the spatial resolution of the line beam light source 214,the light emitting diode devices 400 may be arrayed in a plurality ofcolumns.

FIG. 28A schematically shows the upper surface of the line beam lightsource 214 which includes a plurality of columns of light emitting diodedevices 400 arrayed in Y-axis direction. FIG. 28B is a cross-sectionalview of the line beam light source 214 shown in FIG. 28A taken alongline B-B. FIG. 28B also shows the multilayer stack 100. FIG. 28C is adiagram showing the moving direction of the line beam light source 214relative to the multilayer stack 100.

This line beam light source 214 can also be coupled with the drivingcircuit 280A. The controller 260 controls the operation of the drivingcircuit 280A, thereby temporally and/or spatially modulating thelift-off light radiated from the line beam light source 214.

In this example, the line beam light source 214 includes five columns oflight emitting diode devices 400 each extending in Y-axis direction. Thepositions in Y-axis direction of the five columns of light emittingdiode devices 400 are different from one another. The positions of thelight emitting diode columns are shifted by P/5 in Y-axis directionbetween adjoining columns where P is the array pitch.

This line beam light source 214 includes a lens sheet 420 for converginglight such that one side of the irradiation region formed by each of thelight emitting diode devices 400 has the length of about P/5.Ultraviolet light transmitted through the lens sheet 420 can formirradiation regions in the form of dots over the delamination plane.

As shown in FIG. 28C, when the line beam light source 214 is movedrelative to the multilayer stack 100, a plurality of irradiation regionsoverlap so that the entire delamination plane can be irradiated with theultraviolet light. By modulating the electric current flowing througheach of the light emitting diode devices while the line beam lightsource 214 is moved relative to the multilayer stack 100, spatial andtemporal modulation can be carried out.

FIG. 28D is a diagram schematically showing irradiation regions 218 theline beam source 214 of FIG. 28A is forming. By turning off some of thelight emitting diode devices 400 during scanning by the line beam lightsource 214, non-irradiation regions whose width is smaller than the sizeof the light emitting diode devices 400 can be formed.

FIG. 28E is a plan view showing an example of irradiation regions formedby temporarily modulating the electric current flowing through each ofthe light emitting diode devices 400 during scanning by the line beamsource 214. It is seen that a pattern of irradiation regions andnon-irradiation regions can be formed with high spatial resolution.

Thus, according to the array of the light emitting diode devices 400illustrated in FIG. 28A, modulation with high spatial resolution ispossible as compared with the array of the light emitting diode devices400 illustrated in FIG. 27A.

The irradiation with the lift-off light may be carried out while theplurality of light sources are kept stationary relative to themultilayer stack 100.

FIG. 29 is a top view schematically showing an example of asurface-emission light source 215 in which a large number of lightemitting diode devices 400 are arrayed in a matrix. The number of lightemitting diodes arrayed vertically and horizontally only needs to bearbitrarily set according to the size of the substrate used. In thiscase, a delaminating apparatus applicable to G8-size substrates or hugesubstrates of still larger sizes can be realized. When thesurface-emission light source 215 of this example is used, luminancedistributions of various patterns can be formed as in displays. Thesurface-emission light source 215 may be connected to the drivingcircuit 280, and the driving circuit 280 may be connected to thecontroller 260.

When the irradiation with the lift-off light is carried out while boththe multilayer stack 100 and the surface-emission light source 215 arekept stationary, a precise driving unit for light scanning is notnecessary. When the irradiation with the lift-off light is carried outwhile the multilayer stack 100 is moved relative to a conventionalstationary line beam light source, an area which is at least twice thearea of the multilayer stack 100 is necessary for the movement of themultilayer stack 100. However, according to the embodiment of thepresent disclosure, an extra area for the movement of the multilayerstack 100 is not necessary, and the area for installing the apparatuswill advantageously be halved.

FIG. 30 is a top view schematically showing another example of thesurface-emission light source 215 in which a large number of lightemitting diode devices 400 are arrayed in a matrix. In thesurface-emission light source 215 of this example, the arrangement ofthe light emitting diode devices 400 is determined according to theirradiation regions for the lift-off light.

When the surface-emission light sources 215 shown in FIG. 29 and FIG. 30are used, it is not necessary to carry out lift-off light irradiationwhile the surface-emission light source 215 is kept stationary relativeto the multilayer stack 100. The irradiation with the lift-off light maybe carried out while shifting the relative position of thesurface-emission light source 215 to the multilayer stack 100. While thesurface-emission light source 215 is kept stationary, the shape of thespatial distribution of the irradiation intensity can be changed byshifting the relative position of the surface-emission light source 215to the multilayer stack 100 even if light radiated from thesurface-emission light source 215 forms irradiation regions in the formof dots or lines over the delamination plane. The amount of the shift ofthe relative position of the surface-emission light source 215 to themultilayer stack 100 may be less than, or may be more than, the arraypitch of the light emitting diode devices.

The plane to be delaminated may be divided into a plurality of regions,and each of the regions may be irradiated with a flash of the lift-offlight in the same way as sequential exposure with the use of a stepper.

Thus, using light emitting diode devices enables irradiation with thelift-off light at a lower cost with the use of a large number of lightsources rather than using semiconductor laser devices, which arerelatively expensive. Further, the duration of radiation of the lift-offlight from each of the light emitting diode devices can be easilyincreased. Therefore, even if the optical power of each of the lightemitting diode devices is small, the irradiation energy required fordelamination can be achieved by adjusting the irradiation duration.Furthermore, since laser light is not used, it is also advantageous fromthe viewpoint of safety for human eyes (eye-safe).

<Lift-Off>

FIG. 16A illustrates a state where the multilayer stack 100 is incontact with the stage 210 after irradiation with the lift-off light.While this state is maintained, the distance from the stage 210 to theglass base 10 is increased. At this point in time, the stage 210 of thepresent embodiment holds a light-emitting device portion of themultilayer stack 100.

An unshown actuator holds the glass base 10 and moves the entirety ofthe glass base 10 in the direction of arrow L, thereby carrying outdelaminating (lift-off). The glass base 10 can be moved together with anunshown chuck stage while being adhered by suction to the chuck stage.The direction of movement of the glass base 10 does not need to bevertical, but may be diagonal, to the first surface 100 a of themultilayer stack 100. The movement of the glass base 10 does not need tobe linear but may be rotational. Alternatively, the stage 210 may bemoved upward in the drawing while the glass base 10 is secured by anunshown holder or another stage.

FIG. 16B is a cross-sectional view showing the thus-separated firstportion 110 and second portion 120 of the multilayer stack 100. FIG. 17is a perspective view showing the second portion 120 of the multilayerstack 100. In FIG. 17, a guide rail 246 and other relevant componentsare not shown, and the shape of the intermediate region 30 i issimplified such that the recesses and protrusions are not shown. Thefirst portion 110 of the multilayer stack 100 includes a plurality oflight-emitting devices 1000 which are in contact with the stage 210. Therespective Light-emitting devices 1000 include the functional layerregions 20 and the plurality of flexible substrate regions 30 d of theplastic film 30. Meanwhile, the second portion 120 of the multilayerstack 100 includes the glass base 10 and the intermediate region 30 i ofthe plastic film 30. The intermediate region 30 i of the plastic film 30is bound to the glass base 10 in at least some low-irradiation regions.Thus, the entirety of the intermediate region 30 i of the plastic film30 separates from the stage 210 while the entirety of the intermediateregion 30 i is kept adhered to the glass base 10.

In the example of FIG. 17, both the irradiation process with thelift-off light and the delaminating process are carried out using thedelaminating apparatus 220 that includes the stage 210. The embodimentof the present disclosure is not limited to this example. Theirradiation process with the lift-off light may be carried out using alift-off light irradiation unit which includes the stage 210, while thedelaminating process is carried out using a different apparatus thatincludes another stage which is different from the stage 210. In thiscase, after irradiation with the lift-off light, it is necessary totransfer the multilayer stack 100 from the stage 210 to another unshownstage. When the same stage is used for carrying out both the irradiationprocess with the lift-off light and the delaminating process, the stepof transferring the multilayer stack between the stages can be omitted.

As described above, in the present embodiment, the step of separatingthe multilayer stack 100 into the first portion 110 and the secondportion 120 is carried out while the stage 210 holds the second surface100 b of the multilayer stack 100 by suction. The essence of thisseparation step resides in that an unnecessary part of the multilayerstack 100 which is not a constituent of the light-emitting device 1000separates together with the glass base 10 from the stage 210. In thepresent embodiment, the cutting step illustrated in FIG. 2, i.e., thestep of cutting a part of the multilayer stack 100 exclusive of theglass base 10 into the plurality of light-emitting devices 1000 and theremaining unnecessary portions, is carried out before irradiation withthe lift-off light. Carrying out the cutting step before the lift-offlight irradiation step is effective in realizing the separationillustrated in FIG. 16B and FIG. 17. In order that an unnecessaryportion which is not a constituent of the light-emitting device 1000remains on the glass base 10, the irradiation intensity of the lift-offlight is modulated such that part of that unnecessary portion is keptbound to the glass base 10.

<Steps after Delaminating>

FIG. 18 is a perspective view showing the first portion 110(light-emitting devices 1000) of the multilayer stack 100 adhered bysuction to the stage 210 and the second portion 120 (the glass base 10and objects bound thereto) at a position distant from the stage 210.Unnecessary portions of the multilayer stack 100 which are notconstituents of the light-emitting devices 1000 are bound to the glassbase 10.

FIG. 19 is a perspective view showing the first portion 110 of themultilayer stack 100 adhered by suction to the stage 210. The firstportion 110 of the multilayer stack 100 supported by the stage 210includes a plurality of Light-emitting devices 1000 arrayed in rows andcolumns. In the example of FIG. 19, a part of the plastic film 30,specifically the surface (delaminated surface) 30 s of the flexiblesubstrate regions 30 d, is exposed.

According to the present embodiment, the light-emitting devices 1000 canbe appropriately separated from the remaining unnecessary portions evenwhen the light-emitting devices 1000 and the flexible substrate regions30 d of the plastic film 30 which function as the flexible substratesfor the light-emitting devices 1000 have complicated planar shapes suchas those shown in FIG. 1A and other drawings. As previously described,this is realized by temporally changing the spatial distribution of theirradiation intensity of the lift-off light during scanning with thelift-off light such that an irradiation intensity which is necessary fordelamination is selectively applied to the flexible substrate regions 30d of the plastic film 30. As a result, the entirety of the intermediateregion 30 i of the plastic film 30 can be kept bound to the glass base10.

FIG. 20 is a cross-sectional view showing that the stage 210 holds thelight-emitting devices 1000 by suction. This cross section is parallelto the ZX plane. The direction of the Z-axis of FIG. 20 is opposite tothe direction of the Z-axis of FIG. 18 and FIG. 19.

Various processes can be sequentially or concurrently performed on theplurality of light-emitting devices 1000 which are in contact with thestage 210.

The “processes” to be performed on the light-emitting devices 1000 caninclude attaching a dielectric and/or electrically-conductive film toeach of the plurality of light-emitting devices 1000, cleaning oretching each of the plurality of light-emitting devices 1000, andmounting an optical part and/or an electronic part to each of theplurality of light-emitting devices 1000. Specifically, a part such as,for example, a polarizer, encapsulation film, touchscreen, heatradiation sheet, electromagnetic shield, driver integrated circuit, orthe like, can be mounted to the flexible substrate region 30 d of eachof the light-emitting devices 1000. The sheet-like part includes afunctional film which can add an optical, electrical or magneticfunction to the light-emitting devices 1000.

The plurality of light-emitting devices 1000 are supported by the stage210 such that the light-emitting devices 1000 are adhered by suction tothe stage 210. The various processes which are to be performed on eachof the light-emitting devices 1000 can be efficiently carried out.

The surface 30 s of the plastic film 30 delaminated from the glass base10 is active. Therefore, the surface 30 s may be covered with aprotection film or subjected to a surface treatment for conversion to ahydrophobic surface before various parts are mounted to the surface 30s.

FIG. 21 is a cross-sectional view schematically showing thelight-emitting devices 1000 detached from the stage 210 after thesheet-like part (functional film) 60 is mounted to the light-emittingdevices 1000.

According to the prior art, the plastic film is delaminated from theglass base before the light-emitting devices 1000 are divided from oneanother. Therefore, when a subsequent process is carried out, a largenumber of light-emitting devices 1000 are bound to a single plasticfilm. Thus, it is difficult to carry out an efficient process on each ofthe light-emitting devices 1000. When the light-emitting devices 1000are divided from one another after the sheet-like part is attached, aportion of the sheet-like part which is present in an intermediateregion between adjoining two of the light-emitting devices 1000 isuseless.

On the other hand, according to the embodiment of the presentdisclosure, a large number of light-emitting devices 1000 are stillorderly arrayed on the stage 210 after being delaminated from the glassbase 10. Therefore, various processes can be efficiently performed onthe light-emitting devices 1000 sequentially or concurrently.

After the step of separating the multilayer stack 100 into the firstportion 110 and the second portion 120, the step of adhering anotherprotection sheet (second protection sheet) 70 to the plurality oflight-emitting devices 1000 which are in contact with the stage 210 maybe further performed as shown in FIG. 22. The second protection sheet 70can perform the function of temporarily protecting the surface of theflexible substrate regions 30 d of the plastic film 30 delaminated fromthe glass base 10. The second protection sheet 70 can have the samelaminate structure as that of the previously-described protection sheet50. The protection sheet 50 can be referred to as “first protectionsheet 50”.

The second protection sheet 70 may be adhered to the plurality oflight-emitting devices 1000 after various processes which havepreviously been described are performed on the plurality oflight-emitting devices 1000 which are in contact with the stage 210.

When suction of the light-emitting devices 1000 by the stage 210 isstopped after the second protection sheet 70 is adhered, the pluralityof light-emitting devices 1000 which are bound to the second protectionsheet 70 can be detached from the stage 210. Thereafter, the secondprotection sheet 70 can function as a carrier for the plurality oflight-emitting devices 1000. This is transfer of the light-emittingdevices 1000 from the stage 210 to the second protection sheet 70.Various processes may be sequentially or concurrently performed on theplurality of light-emitting devices 1000 which are bound to the secondprotection sheet 70.

FIG. 23 is a cross-sectional view showing a carrier sheet 90 carrying aplurality of parts (functional films) 80 which are to be mounted to theplurality of light-emitting devices 1000. By moving this carrier sheet90 in the direction of arrow U, the respective parts 80 can be attachedto the light-emitting devices 1000. The upper surface of the parts 80has an adhesive layer which is capable of strongly adhering to thelight-emitting devices 1000. Meanwhile, the adhesion between the carriersheet 90 and the parts 80 is relatively weak. Using such a carrier sheet90 enables a simultaneous “transfer” of the parts 80. Such a transfer isreadily realized because the plurality of light-emitting devices 1000are regularly arrayed on the stage 210 while the light-emitting devices1000 are supported by the stage 210.

Hereinafter, the configuration of the multilayer stack 100 before thedividing of FIG. 2 is described in more detail.

First, see FIG. 24A. FIG. 24A is a cross-sectional view showing theglass base 10 with the plastic film 30 provided on the surface of theglass base 10. The glass base 10 is a supporting substrate forprocesses. The thickness of the glass base 10 can be, for example, about0.3-0.7 mm.

In the present embodiment, the plastic film 30 is a polyimide filmhaving a thickness of, for example, not less than 5 μm and not more than100 μm. The polyimide film can be formed from a polyamide acid, which isa precursor of polyimide, or a polyimide solution. The polyimide filmmay be formed by forming a polyamide acid film on the surface of theglass base 10 and then thermally imidizing the polyamide acid film.Alternatively, the polyimide film may be formed by forming, on thesurface of the glass base 10, a film from a polyimide solution which isprepared by melting a polyimide or dissolving a polyimide in an organicsolvent. The polyimide solution can be obtained by dissolving a knownpolyimide in an arbitrary organic solvent. The polyimide solution isapplied to the surface 109 of the glass base 10 and then dried, wherebya polyimide film can be formed.

In the case of a bottom emission type flexible display, it is preferredthat the polyimide film realizes high transmittance over the entirerange of visible light. The transparency of the polyimide film can berepresented by, for example, the total light transmittance in accordancewith JIS K7105-1981. The total light transmittance can be set to notless than 80% or not less than 85%. On the other hand, in the case of atop emission type flexible display, it is not affected by thetransmittance.

The plastic film 30 may be a film which is made of a synthetic resinother than polyimide. Note that, however, in the embodiment of thepresent disclosure, the process of forming a thin film transistorincludes a heat treatment at, for example, not less than 350° C., andtherefore, the plastic film 30 is made of a material which will not bedeteriorated by this heat treatment.

The plastic film 30 may be a multilayer structure including a pluralityof synthetic resin layers. In one form of the present embodiment, indelaminating a flexible display structure from the glass base 10, laserlift-off is carried out such that the plastic film 30 is irradiated withultraviolet laser light transmitted through the glass base 10. A part ofthe plastic film 30 at the interface with the glass base 10 needs toabsorb the ultraviolet laser light and decompose (disappear).Alternatively, for example, a sacrificial layer (thin metal or amorphoussilicon layer) which is to absorb laser light of a certain wavelengthband and produce a gas may be provided between the glass base 10 and theplastic film 30. In this case, the plastic film 30 can be easilydelaminated from the glass base 10 by irradiating the sacrificial layerwith the laser light. Providing the sacrificial layer also achieves theeffect of suppressing generation of ashes.

<Polishing>

When there is an object (target) which is to be polished away, such asparticles or protuberances, on the surface 30 x of the plastic film 30,the target may be polished away using a polisher such that the surfacebecomes flat. Detection of a foreign object, such as particles, can berealized by, for example, processing of an image obtained by an imagesensor. After the polishing process, a planarization process may beperformed on the surface 30 x of the plastic film 30. The planarizationprocess includes the step of forming a film which improves the flatness(planarization film) on the surface 30 x of the plastic film 30. Theplanarization film does not need to be made of a resin.

<Lower Gas Barrier Film>

Then, a gas barrier film may be formed on the plastic film 30. The gasbarrier film can have various structures. Examples of the gas barrierfilm include a silicon oxide film and a silicon nitride film. Otherexamples of the gas barrier film can include a multilayer film includingan organic material layer and an inorganic material layer. This gasbarrier film may be referred to as “lower gas barrier film” so as to bedistinguishable from a gas barrier film covering the functional layerregions 20, which will be described later. The gas barrier film coveringthe functional layer regions 20 can be referred to as “upper gas barrierfilm”.

<Functional Layer Region>

Hereinafter, the process of forming the functional layer regions 20,including the TFT layer 20A and the light-emitting device layer 20B, andthe upper gas barrier film 40 is described.

First, as shown in FIG. 24B, a plurality of functional layer regions 20are formed on a glass base 10. There is a plastic film 30 between theglass base 10 and the functional layer regions 20. The plastic film 30is bound to the glass base 10.

More specifically, the functional layer regions 20 include a TFT layer20A (lower layer) and a light-emitting device layer 20B (upper layer).The TFT layer 20A and the light-emitting device layer 20B aresequentially formed by a known method. When the light-emitting device isa display, the TFT layer 20A includes a circuit of a TFT array whichrealizes an active matrix. The light-emitting device layer 20B includesan array of light-emitting devices (OLED devices and/or micro LEDdevices), each of which can be driven independently.

The chip size of the micro LED devices is, for example, smaller than 100μm×100 μm. The micro LED devices can be made of different inorganicsemiconductor materials according to the color or wavelength of light tobe radiated. Identical semiconductor chips may include a plurality ofsemiconductor multilayer stacks of different compositions such thatlight of different colors, R (red), G (green) and B (blue), are radiatedfrom the respective semiconductor multilayer stacks. As well known inthe art, a semiconductor chip which radiates ultraviolet light or asemiconductor chip which radiates blue light may be combined withvarious phosphor materials such that light of R, G and B are radiated.

The thickness of the TFT layer 20A is, for example, about 4 μm. Thethickness of the light-emitting device layer 20B including the OLEDdevices is, for example, 1 μm. The thickness of the light-emittingdevice layer 20B including the micro LED devices can be, for example,not less than 10 μm.

FIG. 25 is a basic equivalent circuit diagram of a sub-pixel in adisplay. A single pixel of the display can consist of sub-pixels ofdifferent colors such as, for example, R (red), G (green), and B (blue).The example illustrated in FIG. 25 includes a selection TFT element Tr1,a driving TFT element Tr2, a storage capacitor CH, and a light-emittingdevice EL. The selection TFT element Tr1 is connected with a data lineDL and a selection line SL. The data line DL is a line for transmittingdata signals which define an image to be displayed. The data line DL iselectrically coupled with the gate of the driving TFT element Tr2 viathe selection TFT element Tr1. The selection line SL is a line fortransmitting signals for controlling the ON/OFF state of the selectionTFT element Tr1. The driving TFT element Tr2 controls the state of theelectrical connection between a power line PL and the light-emittingdevice EL. When the driving TFT element Tr2 is ON, an electric currentflows from the power line PL to a ground line GL via the light-emittingdevice EL. This electric current allows the light-emitting device EL toemit light. Even when the selection TFT element Tr1 is OFF, the storagecapacitor CH maintains the ON state of the driving TFT element Tr2.

The TFT layer 20A includes a selection TFT element Tr1, a driving TFTelement Tr2, a data line DL, and a selection line SL. The Light-emittingdevice layer 20B includes a light-emitting device EL. Before formationof the Light-emitting device layer 20B, the upper surface of the TFTlayer 20A is planarized by an interlayer insulating film that covers theTFT array and various wires. A structure which supports thelight-emitting device layer 20B and which realizes active matrix drivingof the light-emitting device layer 20B is referred to as “backplane”.

The circuit elements and part of the lines shown in FIG. 25 can beincluded in any of the TFT layer 20A and the light-emitting device layer20B. The lines shown in FIG. 25 are connected with an unshown drivercircuit.

In the embodiment of the present disclosure, the TFT layer 20A and thelight-emitting device layer 20B can have various specificconfigurations. These configurations do not limit the presentdisclosure. The TFT element included in the TFT layer 20A may have abottom gate type configuration or may have a top gate typeconfiguration. Emission by the light-emitting device included in thelight-emitting device layer 20B may be of a bottom emission type or maybe of a top emission type. The specific configuration of thelight-emitting device is also arbitrary.

The material of a semiconductor layer which is a constituent of the TFTelement includes, for example, crystalline silicon, amorphous silicon,and oxide semiconductor. In the embodiment of the present disclosure,part of the process of forming the TFT layer 20A includes a heattreatment step at 350° C. or higher for the purpose of improving theperformance of the TFT element.

<Upper Gas Barrier Film>

After formation of the above-described functional layer, the entirety ofthe functional layer regions 20 is covered with a gas barrier film(upper gas barrier film) 40 as shown in FIG. 24C. A typical example ofthe upper gas barrier film 40 is a multilayer film including aninorganic material layer and an organic material layer. Elements such asan adhesive film, another functional layer which is a constituent of atouchscreen, polarizers, etc., may be provided between the upper gasbarrier film 40 and the functional layer regions 20 or in a layeroverlying the upper gas barrier film 40. Formation of the upper gasbarrier film 40 can be realized by a Thin Film Encapsulation (TFE)technique. When the light-emitting device layer 20B includes OLEDdevices, from the viewpoint of encapsulation reliability, the WVTR(Water Vapor Transmission Rate) of a thin film encapsulation structureis typically required to be not more than 1×10⁻⁴ g/m²/day. According tothe embodiment of the present disclosure, this criterion is met. Thethickness of the upper gas barrier film 40 is, for example, not morethan 1.5 μm.

FIG. 26 is a perspective view schematically showing the upper surfaceside of the multilayer stack 100 at a point in time when the upper gasbarrier film 40 is formed. A single multilayer stack 100 includes aplurality of light-emitting devices 1000 supported by the glass base 10.In the example illustrated in FIG. 26, a single multilayer stack 100includes a larger number of functional layer regions 20 than in theexample illustrated in FIG. 1A. As previously described, the number offunctional layer regions 20 supported by a single glass base 10 isarbitrary.

<Protection Sheet>

Next, refer to FIG. 24D. As shown in FIG. 24D, a protection sheet 50 isadhered to the upper surface of the multilayer stack 100. The protectionsheet 50 can be made of a material such as, for example, polyethyleneterephthalate (PET), polyvinyl chloride (PVC), or the like. Aspreviously described, a typical example of the protection sheet 50 has alaminate structure which includes a layer of an applied mold-releasingagent at the surface. The thickness of the protection sheet 50 can be,for example, not less than 50 μm and not more than 200 μm.

After the thus-formed multilayer stack 100 is provided, the productionmethod of the present disclosure can be carried out using theabove-described production apparatus (delaminating apparatus 220).

INDUSTRIAL APPLICABILITY

An embodiment of the present invention provides a novel flexiblelight-emitting device production method. A flexible light-emittingdevice is broadly applicable to smartphones, tablet computers, on-boarddisplays, and small-, medium- and large-sized television sets. Theflexible light-emitting device can also be used as an illuminationdevice.

REFERENCE SIGNS LIST

10 . . . glass base, 20 . . . functional layer region, 20A . . . TFTlayer, 20B . . . light-emitting device layer, 30 . . . plastic film, 30d . . . flexible substrate region of plastic film, 30 i . . .intermediate region of plastic film, 40 . . . gas barrier film, 50 . . .protection sheet, 100 . . . multilayer stack, 210 . . . stage, 220 . . .lift-off light irradiation unit (delaminating apparatus), 260 . . .controller, 300 . . . semiconductor laser device, 1000 . . .light-emitting device

1. A method for producing a flexible light-emitting device, comprising:providing a multilayer stack which has a first surface and a secondsurface, the multilayer stack including a glass base which defines thefirst surface, a functional layer region including a TFT layer and alight-emitting device layer, a synthetic resin film provided between theglass base and the functional layer region and bound to the glass base,the synthetic resin film including a flexible substrate regionsupporting the functional layer region and an intermediate regionsurrounding the flexible substrate region, and a protection sheet whichcovers the functional layer region and which defines the second surface;dividing the intermediate region and the flexible substrate region ofthe synthetic resin film from each other; irradiating an interfacebetween the synthetic resin film and the glass base with lift-off light;and separating the multilayer stack into a first portion and a secondportion by increasing a distance from a stage to the glass base whilethe second surface of the multilayer stack is kept in contact with thestage, wherein the first portion of the multilayer stack includes alight-emitting device which is in contact with the stage, thelight-emitting device including the functional layer region and theflexible substrate region of the synthetic resin film, the secondportion of the multilayer stack includes the glass base and theintermediate region of the synthetic resin film, and irradiating theinterface between the synthetic resin film and the glass base with thelift-off light includes: forming the lift-off light from a plurality ofarranged light sources and temporally and spatially modulating a powerof the plurality of light sources according to a shape of the flexiblesubstrate region of the synthetic resin film; reducing an irradiationintensity of the lift-off light for at least part of an interfacebetween the intermediate region of the synthetic resin film and theglass base below a threshold level Th of the irradiation intensity whichis necessary for delamination; irradiating the at least part of theinterface between the intermediate region of the synthetic resin filmand the glass base with the lift-off light, and irradiating theinterface between the flexible substrate region of the synthetic resinfilm and the glass base with the lift-off light whose irradiationintensity is higher than threshold level Th.
 2. The method of claim 1,wherein the lift-off light is incoherent light.
 3. The method of claim1, wherein the light-emitting device layer includes a plurality ofarrayed micro LEDs, and the lift-off light is laser light.
 4. The methodof any claim 1, wherein a shape of the flexible substrate region of thesynthetic resin film has a cutout, a protrusion, and/or a curved contourwhen viewed in a direction perpendicular to the first surface.
 5. Themethod of claim 1, wherein a number of the flexible substrate region ofthe synthetic resin film is plural, and a number of the light-emittingdevice included in the first portion of the multilayer stack is plural.6. The method of claim 1, wherein the plurality of light sources are aplurality of light emitting diode devices, and irradiating the interfacebetween the synthetic resin film and the glass base with the lift-offlight includes modulating a driving current flowing through each of theplurality of light emitting diode devices, thereby temporally and/orspatially modulating the irradiation intensity of the lift-off light. 7.The method of claim 6, wherein the plurality of light emitting diodedevices are arranged in a single row or a plurality of rows.
 8. Themethod of claim 7, wherein an arrangement pitch of the plurality oflight emitting diode devices is in a range of not less than 3 mm and notmore than 10 mm.
 9. The method of claim 1, wherein the lift-off light isa line beam extending in a first direction which is parallel to aperimeter of the glass base, and irradiating the interface between thesynthetic resin film and the glass base with the lift-off light includesmoving an irradiation region on the interface which is to be irradiatedwith the lift-off light in a second direction which is transverse to thefirst direction.
 10. The method of claim 1, wherein the lift-off lightis plane-like light extending in a first direction and a seconddirection, the first direction being parallel to a perimeter of theglass base, the second direction being transverse to the firstdirection, and irradiating the interface between the synthetic resinfilm and the glass base with the lift-off light includes moving ornot-moving irradiation region on the interface which is to be irradiatedwith the lift-off light.
 11. The method of claim 9, wherein the at leastpart of the interface between the intermediate region of the syntheticresin film and the glass base includes a plurality of parallel striperegions extending in the first direction, and any of the plurality ofparallel stripe regions includes a large-width portion and/or anarrow-width portion.
 12. The method of claim 9, wherein the at leastpart of the interface between the intermediate region of the syntheticresin film and the glass base includes a plurality of parallel striperegions extending in the second direction, and any of the plurality ofparallel stripe regions includes a large-width portion and/or anarrow-width portion.
 13. The method of claim 1, wherein the at leastpart of the interface between the intermediate region of the syntheticresin film and the glass base has a width which is not less than 50% ofa width of the intermediate region.
 14. The method of claim 1, whereinthe at least part of the interface between the intermediate region ofthe synthetic resin film and the glass base has a width which is notless than 1 mm.
 15. The method of claim 1, wherein the differencebetween an irradiation intensity of the lift-off light in the at leastpart of the interface between the intermediate region of the syntheticresin film and the glass base and an irradiation intensity of thelift-off light for the interface between the flexible substrate regionof the synthetic resin film and the glass base is not less than 50mJ/cm².
 16. The method of claim 1 further comprising, after separatingthe multilayer stack into the first portion and the second portion,performing a process on the light-emitting device which is in contactwith the stage, wherein the process includes attaching a dielectricand/or electrically-conductive film to the light-emitting device,cleaning or etching the plurality of light-emitting device, and mountingan optical part and/or an electronic part to the light-emitting device.17. An apparatus for producing a flexible light-emitting device,comprising: a stage for supporting a multilayer stack which has a firstsurface and a second surface, the multilayer stack including a glassbase which defines the first surface, a functional layer regionincluding a TFT layer and a light-emitting device layer, a syntheticresin film provided between the glass base and the functional layerregion and bound to the glass base, the synthetic resin film including aflexible substrate region supporting the functional layer region and anintermediate region surrounding the flexible substrate region, and aprotection sheet which covers the functional layer region and whichdefines the second surface, the intermediate region and the flexiblesubstrate region of the synthetic resin film being divided from eachother; and a lift-off light irradiation unit for irradiating withlift-off light an interface between the synthetic resin film and theglass base in the multilayer stack supported by the stage, wherein thelift-off light irradiation unit includes a plurality of arranged lightsources for forming the lift-off light, and the lift-off lightirradiation unit configured to: modulating temporally and spatially apower of the plurality of light sources according to a shape of theflexible substrate region of the synthetic resin film such that anirradiation intensity of the lift-off light for at least part of aninterface between the intermediate region of the synthetic resin filmand the glass base is lower than a threshold level Th of the irradiationintensity which is necessary for delamination; irradiate the at leastpart of the interface between the intermediate region of the syntheticresin film and the glass base with the lift-off light; and irradiate theinterface between the flexible substrate region of the synthetic resinfilm and the glass base with the lift-off light whose irradiationintensity is higher than threshold level Th.
 18. The apparatus of claim17, wherein each of the plurality of arranged light sources is anincoherent light source.
 19. The apparatus of claim 17, wherein thelight-emitting device layer includes a plurality of arrayed micro LEDs,and each of the plurality of light sources is a semiconductor laserdevice.
 20. The apparatus of claim 17, wherein the plurality of lightsources are a plurality of light emitting diode devices, and thelift-off light irradiation unit includes a driving circuit formodulating a driving current flowing through each of the plurality oflight emitting diode devices, thereby temporally and/or spatiallymodulating the irradiation intensity of the lift-off light.
 21. Theapparatus of claim 20, wherein the plurality of light emitting diodedevices are arranged in a single row or a plurality of rows.
 22. Theapparatus of claim 21, wherein an arrangement pitch of the plurality oflight emitting diode devices is in a range of not less than 3 mm and notmore than 10 mm.
 23. The apparatus of claim 17, further comprising anactuator for increasing a distance from the stage to the glass basewhile the stage is kept in contact with the second surface of themultilayer stack, thereby separating the multilayer stack into a firstportion and a second portion, wherein the first portion of themultilayer stack includes a light-emitting device which is in contactwith the stage, the light-emitting device including the functional layerregion and the flexible substrate region of the synthetic resin film,and the second portion of the multilayer stack includes the glass baseand the intermediate region of the synthetic resin film.
 24. (canceled)